DIN 1.1191 / C45E Forged Steel Round Bar

Contact Now* Send an Inquiry to this supplier.
or
Start Order * Name your price

Contact us

Wuxi Fuhong Special Steel Co.,Ltd
[China]

Address
Luoshe Wuxi Jiangsu
Phone
86-0510-83302896
Contact name
Hunter Hu

Quick Information

  • Brand Name: Fuhong Steel
  • Place of Origin: China
  • Model Number : 1.1191 / C45E
  • Application : Tool Steel Bar
  • Dimensions : Dia 100-1000mm
  • Steel Grade : 1.1191 / C45E
  • Technique : Forged
  • Type : Carbon Steel Bar

Description

1.1191 / C45E

DIN 1.1191 / C45E Steel is a general carbon engineering steel according to DIN Germany standard. It's one kind of high strength carbon steel which is mainly used after quenched and tempered. The 1.1191 steel has a certain shape and toughness and high strength. After QT, C45E steel can obtain good comprehensive mechanical properties. The welding performance of 1.1191 steel is not so good. This material needs to be preheated before welding, and carry on the annealing treatment after welding in order to eliminate the welding stress.

Chemical Composition
C: 0.42-0.50; Si: max0.40; Mn: 0.50-0.80; P: max0.030; S: max0.035;
Cr: max0.40; Ni: max0.40; Mo: max0.10;

Equivalent Grades
AISI/ASTM: 1045
Germany: CK45
BS: 080M46
JIS: S45C
UNI: C45

Form of 1.1191 Steel
Round / Square / Flat Bars, Shafts, Rollers, Blocks

Size of C45E Steel
- As Forged
Round bar
Size: Dia.80-1,000mm
Length: 3,000-10,000mm
Square bar
Size: 150×150-600×600mm
Length: 3,000-8,000mm
(Forged Flat Bars, Shafts, Rollers and Blocks can be Customized)
- As Rolled
Round Bar
Size: Dia.10-300mm
Length: 3,000-10,000mm(can be Customized)

Surface Condition
Black, Rough Machined, Turned

Hardness of 1.1191 Steel
Annealed (+A): max 197HB
As Rolled and Turned (+SH): 172-242HB

Mechanical Properties of C45E+QT
Tensile strength: 600MPa
Yield point: 355MPa
Percentage reduction of area after fracture: 40%
Elongation after fracture: 16%
Impact test(+20°C): Transverse - 14J; Longitud - 39J

Quenched and Tempered (+QT) of W-Nr 1.1191 Steel
1. Increase the temperature slowly up to 840°C;
2. Soak at this hardening temperature and quench 1.1191 steel in the oil;
3. Cool down to 20°C in the air;
4. Heat uniformly to the tempering temperature of 600°C;
5. Hold at this temperature for 2 hours per 25mm thickness
6. Withdraw from the furnace and cool in the air.

Normalizing (+N) of DIN C45E Steel
1)Heating din 1.1191 to 850°C;
2)Cool C45E material down to 20°C quickly in the air.

Applications of 1.1191 / C45E Steel
DIN 1.1191 steel is applied to manufacture high strength movement parts,such as air compressor,piston pump,the impeller of a steam turbine,heavy duty and general machinery of the rolling shaft,connecting rod,worm,rack,gear,etc.

Contact Info
- To: Mr Hunter Hu
- Skype: sinohss

- URL: www.steel-bar.com


Price

  • Price Condition : FOB
  • Price : USD600 / Ton
  • Delivery Port : Shanghai

Packaging & Delivery

  • Packing :1.1191 / C45E Steel Bars: Seaworthy Package
  • Delivery Lead Time : 50Days, Email:fuhongsteel@gmail.com
  • Minimum Order : 10Ton
  • Supply Ability : 1.1191 / C45E Forged Round Bar:1000Tons/Month

Product Image

  • DIN 1.1191 / C45E Forged Steel Round Bar image

Send an Inquiry to this supplier

Send an Inquiry to this supplier
* From
  To Hunter Hu
Wuxi Fuhong Special Steel Co.,Ltd
* Buying Product
- Please enter your specific buying item.
e.g. 42 inch LCD TV, leather executive chair
Category : Steel Round Bars
* Message

Use English only Max. 2000 characters. (Min. 20)

Send
EC21.com does not guarantee the validity of product information or the credentials of sellers.